<span id="n9ldx"></span>
<span id="n9ldx"><video id="n9ldx"><strike id="n9ldx"></strike></video></span>
<th id="n9ldx"></th>
<span id="n9ldx"><video id="n9ldx"></video></span>
<th id="n9ldx"><noframes id="n9ldx"><span id="n9ldx"></span><th id="n9ldx"></th>
<span id="n9ldx"><video id="n9ldx"></video></span>
<th id="n9ldx"></th><span id="n9ldx"><noframes id="n9ldx"><span id="n9ldx"></span>
<th id="n9ldx"></th>
<span id="n9ldx"><noframes id="n9ldx">
<span id="n9ldx"><noframes id="n9ldx"><strike id="n9ldx"><video id="n9ldx"></video></strike>
<th id="n9ldx"></th>
<progress id="n9ldx"><video id="n9ldx"></video></progress>
<th id="n9ldx"><video id="n9ldx"></video></th><span id="n9ldx"><video id="n9ldx"><span id="n9ldx"></span></video></span>
<span id="n9ldx"></span>
<th id="n9ldx"></th>
<th id="n9ldx"><noframes id="n9ldx"><span id="n9ldx"></span>
歡迎來到山東易安換熱設備有限公司網站,我們將竭誠為您服務! 網站首頁|聯系我們

管殼式換熱器的腐蝕都有哪些類型?

更新時間:23/08/08 16:05:08   分    享:
  我們在使用管殼式換熱器的時候,不可避免的會遇到設備腐蝕的情況,這一情況的出現嚴重的影響了設備的生產效率。那么換熱器腐蝕的種類都有哪些?下面小編給大家介紹下。
  1、均勻腐蝕:接觸介質的金屬表面全部或大部分被腐蝕的現象,這是由于板片選材不當或使用時間過長,超過了允許使用壽命而造成的。
  2、露點腐蝕:主要是由含有酸性物質的熱蒸汽與冷板片接觸而造成的。
  3、點蝕:主要是由局部腐蝕造成的局部金屬表面的鈍化膜破壞,形成尺寸小于1mm的穿孔或蝕坑。
  4、磨蝕:板片的介質入口角孔處和導流區的流速過高,或流體中含有砂粒類顆粒物時會導致磨蝕。
  5、縫隙腐蝕:這是一種呈斑點狀或潰瘍形的局部腐蝕,腐蝕主要產生在管殼式換熱器金屬零件的縫隙處,由于滯留介質的電化學不均勻性導致的,主要發生在密封墊片槽底或板片封閉流道的角孔墊片外側。
  6、微生物腐蝕:海水中的藻類、細菌、原生物等,可導致板片的微生物腐蝕。
  7、應力腐蝕開裂:在靜態拉伸應力與電化學介質的共同作用下,由陰極溶解過程引起的金屬局部腐蝕裂紋或斷裂,板片壓制成型時會產生殘余內應力,若與介質中的鹵素離子或H2S接觸可能引起應力腐蝕開裂。
  8、晶間腐蝕:起源于金屬表面并沿晶粒邊界深入到內部的腐蝕,可導致晶粒間的結合力喪失,使材料的強度大大降低。
  管殼式換熱器的腐蝕類型就為您介紹到這里,如果您想了解更多相關知識的話,可以持續關注我站。